17-4PH
Characteristics
17-4PH is a precipitation hardening stainless steel with combustion resistance and corrosion resistance equivalent to SUS304, and high strength and hardness can be obtained by subjecting it to heat treatment. Because the aging process of 17-4PH can be conducted at low temperatures, no large strain is likely to result, thus being used for applications such as a long shaft.
Stock Form and Sizes
◆1000mm ◎2000mm ▲3000mm ■3500mm ●4000mm ★2500mm~3990mm
17-4PHPeeled round bars(ST)Specification:ASTM A564、ASME SA564、AMS 5643
size 10〜27 | ||||||||||||||
---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
10 | 12 | 13 | 14 | 15 | 16 | 17 | 18 | 19 | 20 | 22 | 24 | 25 | 26 | 27 |
● (h9) | ● (h9) | ● (h9) | ★ | ★ | ★ | ★ | ||||||||
size 28〜55 | ||||||||||||||
28 | 30 | 32 | 33 | 35 | 36 | 38 | 40 | 42 | 44 | 45 | 46 | 48 | 50 | 55 |
★ | ★ | ★ | ★ | ★ | ★ | |||||||||
size 60〜160 | ||||||||||||||
60 | 65 | 70 | 75 | 80 | 85 | 90 | 95 | 100 | 110 | 120 | 130 | 140 | 150 | 160 |
★ | ★ | ★ | ★ | ★ | ★ | ★ | ★ 135 | ★ | ★ | |||||
size 170〜200 | ||||||||||||||
170 | 180 | 190 | 200 | |||||||||||
★ | ★ |
Chemical composition
Ni | Cr | Fe | C | Mn | Si | Co | P | S | Mo | Cu | N | Nb | Ta | Nb+Ta | W | V | other | |
---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|---|
min | 3.00 | 15.00 | 3.00 | 0.15 | ||||||||||||||
max | 5.00 | 17.50 | 0.07 | 1.00 | 1.00 | 0.040 | 0.030 | 5.00 | 0.45 |
※Above is standard values of ASTM A564. For further information, please contact us.
Mechanical properties
17-4PH A
Tensile Strength Mpa | 0.2% Yield Strength Mpa | Elongation % | Reduction of Area % | Hardness | |
---|---|---|---|---|---|
min | |||||
max | HB363 |
17-4PH H900 Below 3″(76.2mm)
Tensile Strength Mpa | 0.2% Yield Strength Mpa | Elongation % | Reduction of Area % | Hardness | |
---|---|---|---|---|---|
min | 1310 | 1170 | 10 | 40 | HB388 |
max |
17-4PH H900 76.2~203.2㎜
Tensile Strength Mpa | 0.2% Yield Strength Mpa | Elongation % | Reduction of Area % | Hardness | |
---|---|---|---|---|---|
min | 1310 | 1170 | 10 | 35 | HB388 |
max |
17-4PH H1025 Below 8″(203.2mm)
Tensile Strength Mpa | 0.2% Yield Strength Mpa | Elongation % | Reduction of Area % | Hardness | |
---|---|---|---|---|---|
min | 1070 | 1000 | 12 | 45 | HB331 |
max |
17-4PH H1075 Below 8″(203.2mm)
Tensile Strength Mpa | 0.2% Yield Strength Mpa | Elongation % | Reduction of Area % | Hardness | |
---|---|---|---|---|---|
min | 1000 | 860 | 13 | 45 | HB311 |
max |
17-4PH H1150
Tensile Strength Mpa | 0.2% Yield Strength Mpa | Elongation % | Reduction of Area % | Hardness | |
---|---|---|---|---|---|
min | 930 | 725 | 16 | 50 | HB277 |
max |
17-4PH H1150D
Tensile Strength Mpa | 0.2% Yield Strength Mpa | Elongation % | Reduction of Area % | Hardness | |
---|---|---|---|---|---|
min | 860 | 725 | 16 | 50 | HB255 |
max | HB311 |
※Above is standard values of ASTM A564. For further information, please contact us.
International Specification Comparison chart
Material | Round bars | Plates/Sheets | Pipes/Tubes | ||
---|---|---|---|---|---|
Seamless | Welded | ||||
JIS | SUS630 | G4303/G4318 | G4304/G4305 | ||
ASTM | S17400 | A564 | A693 | ||
ASME | S17400 | SA546 | SA693 | ||
DIN/EN | 1.4542 |
- Disclaimer
- All the information on this website is published in good faith and for general information purpose only and not for technical design purposes. We do not make any warranties about the completeness, reliability and accuracy of this information. Any action you take upon the information on our website is strictly at your own risk. and we will not be liable for any losses and damages in connection with the use of our website.